Natland, James H; Mahoney, John J (1982): (Table 1) Sample descriptions and mineralogy at DSDP Holes 60-458 and 60-459B [dataset]. PANGAEA, https://doi.org/10.1594/PANGAEA.820227, In supplement to: Natland, JH; Mahoney, JJ (1982): Alteration of igneous rocks at Deep Sea Drilling Project Sites 458 and 459, Mariana fore-arc region: Relationship to basement structure. In: Hussong, DM; Uyeda, S; et al. (eds.), Initial Reports of the Deep Sea Drilling Project (U.S. Govt. Printing Office), 60, 769-788, https://doi.org/10.2973/dsdp.proc.60.145.1982
Always quote citation above when using data! You can download the citation in several formats below.
Project(s):
Deep Sea Drilling Project (DSDP)
Coverage:
Median Latitude: 17.863350 * Median Longitude: 147.117900 * South-bound Latitude: 17.862500 * West-bound Longitude: 146.934300 * North-bound Latitude: 17.864200 * East-bound Longitude: 147.301500
Date/Time Start: 1978-04-18T00:00:00 * Date/Time End: 1978-04-25T00:00:00
Minimum Elevation: -4121.0 m * Maximum Elevation: -3447.0 m
Event(s):
60-458 * Latitude: 17.864200 * Longitude: 146.934300 * Date/Time: 1978-04-18T00:00:00 * Elevation: -3447.0 m * Penetration: 465.5 m * Recovery: 97.6 m * Location: North Pacific/TRENCH * Campaign: Leg60 * Basis: Glomar Challenger * Method/Device: Drilling/drill rig (DRILL) * Comment: 46 cores; 437 m cored; 28.5 m drilled; 22.3 % recovery
60-459B * Latitude: 17.862500 * Longitude: 147.301500 * Date/Time: 1978-04-25T00:00:00 * Elevation: -4121.0 m * Penetration: 691.5 m * Recovery: 176.2 m * Location: North Pacific/SEDIMENT POND * Campaign: Leg60 * Basis: Glomar Challenger * Method/Device: Drilling/drill rig (DRILL) * Comment: 68 cores; 644 m cored; 28.5 m drilled; 27.4 % recovery
Comment:
In many samples plagioclase was a prominent constituent. We have ignored it, supposing it to be a contaminant inadvertently scraped from walls of joints, or an unaltered remnant. X = present; - = not present.
Parameter(s):
# | Name | Short Name | Unit | Principal Investigator | Method/Device | Comment |
---|---|---|---|---|---|---|
1 | Event label | Event | ||||
2 | Sample code/label | Sample label | Natland, James H | DSDP/ODP/IODP sample designation | ||
3 | Description | Description | Natland, James H | |||
4 | Palygorskite | Plg | Natland, James H | X-ray diffraction (XRD) | ||
5 | Celadonite | Cel | Natland, James H | X-ray diffraction (XRD) | ||
6 | Smectite | Sme | Natland, James H | X-ray diffraction (XRD) | Trioctahedral | |
7 | Smectite | Sme | Natland, James H | X-ray diffraction (XRD) | Dioctahedral | |
8 | Smectite | Sme | Natland, James H | X-ray diffraction (XRD) | Mixed | |
9 | Smectite | Sme | Natland, James H | X-ray diffraction (XRD) | Undifferentiated | |
10 | Phillipsite | Php | Natland, James H | X-ray diffraction (XRD) | ||
11 | Clinoptilolite | Cpt | Natland, James H | X-ray diffraction (XRD) | ||
12 | Calcite | Cal | Natland, James H | X-ray diffraction (XRD) | ||
13 | Quartz | Qz | Natland, James H | X-ray diffraction (XRD) |
License:
Creative Commons Attribution 3.0 Unported (CC-BY-3.0)
Size:
515 data points
Data
1 Event | 2 Sample label (DSDP/ODP/IODP sample designation) | 3 Description | 4 Plg (X-ray diffraction (XRD)) | 5 Cel (X-ray diffraction (XRD)) | 6 Sme (Trioctahedral, X-ray diffract...) | 7 Sme (Dioctahedral, X-ray diffracti...) | 8 Sme (Mixed, X-ray diffraction (XRD)) | 9 Sme (Undifferentiated, X-ray diffr...) | 10 Php (X-ray diffraction (XRD)) | 11 Cpt (X-ray diffraction (XRD)) | 12 Cal (X-ray diffraction (XRD)) | 13 Qz (X-ray diffraction (XRD)) |
---|---|---|---|---|---|---|---|---|---|---|---|---|
60-458 | 60-458-28-1,19-23 | Pale green coating on fracture surface | X | - | - | - | - | - | X | - | - | - |
60-458 | 60-458-28-1,106-107 | White fracture coating | - | - | - | X | - | - | X | - | - | - |
60-458 | 60-458-29-2,18-20 | Slickensided dark green fracture coating | - | - | X | - | - | - | X | - | - | - |
60-458 | 60-458-29-2,87-89 | Vesicle filling | - | - | - | - | X | - | - | - | - | - |
60-458 | 60-458-29-2,106-108 | Tan crack filling | - | - | - | - | - | - | - | - | X | - |
60-458 | 60-458-32-2,8-9 | - | - | - | - | - | - | - | - | X | - | |
60-458 | 60-458-33-1,29-31 | Altered basalt | - | - | - | X | - | - | - | - | X | - |
60-458 | 60-458-34-2,35 | Altered basalt | - | - | - | - | - | - | - | - | X | - |
60-458 | 60-458-36-1,100 | Altered basalt | - | - | - | X | - | - | X | - | - | - |
60-458 | 60-458-39,69-88 | Fracture coating | - | - | - | - | - | X | X | - | - | - |
60-458 | 60-458-40-1,32-33 | Green black fracture filling | - | - | - | X | - | - | X | - | - | - |
60-458 | 60-458-41-1,50-51 | Highly altered basalt | - | - | - | X | - | - | - | - | - | - |
60-458 | 60-458-44-1,29-30 | Fracture filling in pillow rind | - | - | - | - | - | X | X | - | - | - |
60-458 | 60-458-44-1,115-116 | Muddy alteration material | - | - | - | - | X | - | - | - | - | - |
60-458 | 60-458-46-1,99-100 | White crack filling in pillow fragment | - | - | - | X | - | - | X | - | - | - |
60-458 | 60-458-49-1,29-32 | Green coating on fracture surface | - | - | - | - | X | - | - | - | - | - |
60-458 | 60-458-49-1,125-127 | White hyaloclastite fragment | - | - | - | - | - | X | - | - | - | - |
60-459B | 60-459B-60-2,52-53 | Pink coating on fracture surface | - | - | X | - | - | - | - | - | - | - |
60-459B | 60-459B-61-1,3-5 | Pink coating on fracture surface | - | - | X | - | - | - | - | - | - | - |
60-459B | 60-459B-61-2,76-77 | Grey coating on fracture surface | X | - | - | - | - | X | - | - | - | - |
60-459B | 60-459B-61-2,87-88 | Green coating on fracture surface | X | - | - | - | - | - | - | - | - | - |
60-459B | 60-459B-61-2,90-91 | Green coating on fracture surface | X | - | - | - | - | X | - | - | - | - |
60-459B | 60-459B-62-1,3-4 | Reddish coating on fracture surface | X | - | - | - | - | X | - | - | - | - |
60-459B | 60-459B-62-1,79-80 | Green coating on fracture surface | X | - | - | - | - | - | - | - | - | - |
60-459B | 60-459B-63-1,52-53 | Greenish coating on fracture surface | X | - | - | - | - | - | - | - | - | - |
60-459B | 60-459B-64-1,42-44 | Greenish black groundmass alteration material | - | - | X | - | - | - | X | - | X | - |
60-459B | 60-459B-65-1,35-37 | Green cavity filling | - | - | - | - | X | - | X | - | - | - |
60-459B | 60-459B-65-1,40-46 | Green vein filling | - | - | - | - | - | X | X | X | - | - |
60-459B | 60-459B-65-1,132-133 | Altered basalt | - | - | - | - | - | X | - | - | - | - |
60-459B | 60-459B-66-1,4-5 | Green coating on fracture surface | X | - | - | - | - | - | - | - | - | - |
60-459B | 60-459B-66-1,133-136 | Dark green coating on fracture surface | X | - | - | - | - | - | - | - | - | - |
60-459B | 60-459B-66-2,101-103 | Greenish coating on fracture surface | X | - | - | - | - | - | - | - | - | - |
60-459B | 60-459B-66-3,42-45 | Altered chips of basalt | - | - | - | - | - | X | - | - | - | X |
60-459B | 60-459B-67-1,3-4 | Pillow rind alteration material | - | - | - | - | - | X | - | - | - | - |
60-459B | 60-459B-67-1,145-146 | Bright blue-green fracture coating | - | X | - | - | - | - | - | - | - | - |
60-459B | 60-459B-69-2,121-122 | Light green fracture coating | - | - | X | - | - | - | X | - | - | - |
60-459B | 60-459B-69-3,29-31 | Gray green coating on fracture surface | X | - | X | - | - | - | - | - | - | - |
60-459B | 60-459B-69-3,64-66 | Greenish friable alteration material | - | - | - | - | - | X | - | - | - | - |
60-459B | 60-459B-71-1,102-104 | Green gray vein filling | X | - | X | - | - | - | - | - | - | - |
60-459B | 60-459B-71-1,147-148 | Green gray vein filling | X | - | - | - | - | X | - | - | X | - |
60-459B | 60-459B-71-2,130-131 | Green gray veing filling | X | - | - | - | - | - | - | - | - | - |
60-459B | 60-459B-73-1,90-92 | From hyaloclastite zone | - | - | - | - | X | - | X | - | - | - |
60-459B | 60-459B-73-2,53-55 | Greenish cemented breccia | - | - | - | - | - | X | - | - | - | - |