Sawyer, Dale S; Whitmarsh, Robert B; Shipboard Scientific Party (2005): X-ray fluorescence on samples of ODP Hole 149-900A [dataset]. PANGAEA, https://doi.org/10.1594/PANGAEA.271370
Always quote citation above when using data! You can download the citation in several formats below.
Related to:
ODP/TAMU (2005): JANUS Database. Ocean Drilling Program, Texas A&M University, College Station TX 77845-9547, USA; (data copied from Janus 2005-02 to 2005-06), http://www-odp.tamu.edu/database/
Sawyer, Dale S; Whitmarsh, Robert B; Klaus, Adam; et al. (1994): Proceedings of the Ocean Drilling Program, 149 Initial Reports. Proceedings of the Ocean Drilling Program, Ocean Drilling Program, 149, 719 pp, https://doi.org/10.2973/odp.proc.ir.149.1994
Project(s):
Ocean Drilling Program (ODP)
Coverage:
Latitude: 40.683200 * Longitude: -11.604200
Date/Time Start: 1993-05-11T19:30:00 * Date/Time End: 1993-05-22T15:00:00
Minimum DEPTH, sediment/rock: 749.12 m * Maximum DEPTH, sediment/rock: 792.53 m
Event(s):
149-900A * Latitude: 40.683200 * Longitude: -11.604200 * Date/Time Start: 1993-05-11T19:30:00 * Date/Time End: 1993-05-22T15:00:00 * Elevation: -5049.0 m * Penetration: 805 m * Recovery: 519.61 m * Location: South Atlantic Ocean * Campaign: Leg149 * Basis: Joides Resolution * Method/Device: Drilling/drill rig (DRILL) * Comment: 86 cores; 804.5 m cored; 0 m drilled; 64.6 % recovery
Parameter(s):
# | Name | Short Name | Unit | Principal Investigator | Method/Device | Comment |
---|---|---|---|---|---|---|
1 | DEPTH, sediment/rock | Depth sed | m | Geocode | ||
2 | Depth, composite | Depth comp | mcd | Shipboard Scientific Party | ||
3 | Sample code/label | Sample label | Shipboard Scientific Party | DSDP/ODP/IODP sample designation | ||
4 | Sample comment | Sample comment | Shipboard Scientific Party | X-ray fluorescence (XRF) | ||
5 | Loss on ignition | LOI | % | Shipboard Scientific Party | X-ray fluorescence (XRF) | Bead_loi |
6 | Silicon dioxide | SiO2 | % | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
7 | Titanium dioxide | TiO2 | % | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
8 | Aluminium oxide | Al2O3 | % | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
9 | Iron oxide, Fe2O3 | Fe2O3 | % | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
10 | Manganese oxide | MnO | % | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
11 | Magnesium oxide | MgO | % | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
12 | Calcium oxide | CaO | % | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
13 | Sodium oxide | Na2O | % | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
14 | Potassium oxide | K2O | % | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
15 | Phosphorus pentoxide | P2O5 | % | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
16 | Niobium | Nb | mg/kg | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
17 | Zirconium | Zr | mg/kg | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
18 | Yttrium | Y | mg/kg | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
19 | Strontium | Sr | mg/kg | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
20 | Rubidium | Rb | mg/kg | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
21 | Zinc | Zn | mg/kg | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
22 | Copper | Cu | mg/kg | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
23 | Nickel | Ni | mg/kg | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
24 | Chromium | Cr | mg/kg | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
25 | Vanadium | V | mg/kg | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
26 | Cerium | Ce | mg/kg | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
27 | Barium | Ba | mg/kg | Shipboard Scientific Party | X-ray fluorescence (XRF) | |
28 | Comment | Comment | Shipboard Scientific Party | X-ray fluorescence (XRF) |
License:
Creative Commons Attribution 3.0 Unported (CC-BY-3.0)
Size:
479 data points
Data
1 Depth sed [m] | 2 Depth comp [mcd] | 3 Sample label | 4 Sample comment | 5 LOI [%] | 6 SiO2 [%] | 7 TiO2 [%] | 8 Al2O3 [%] | 9 Fe2O3 [%] | 10 MnO [%] | 11 MgO [%] | 12 CaO [%] | 13 Na2O [%] | 14 K2O [%] | 15 P2O5 [%] | 16 Nb [mg/kg] | 17 Zr [mg/kg] | 18 Y [mg/kg] | 19 Sr [mg/kg] | 20 Rb [mg/kg] | 21 Zn [mg/kg] | 22 Cu [mg/kg] | 23 Ni [mg/kg] | 24 Cr [mg/kg] | 25 V [mg/kg] | 26 Ce [mg/kg] | 27 Ba [mg/kg] | 28 Comment |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
749.12 | 749.12 | 149-900A-80R-1,22-25 | RUN CAB; REP P | 10 | 16 | 0 | 416 | 10 | 15 | 0 | 158 | 10 | 16 | 26 | 104 | HARDROCK | |||||||||||
749.12 | 749.12 | 149-900A-80R-1,22-25 | RUN CAD; REP A | 3.83 | 50.41 | 26.26 | 2.84 | 0.07 | 5.46 | 10.21 | 3.07 | 0.91 | 0.02 | HARDROCK-after XRF upgrade | |||||||||||||
749.60 | 749.60 | 149-900A-80R-1,70-73 | RUN CAJ; REP P | 11 | 14 | 1 | 309 | 12 | 19 | 16 | 113 | 234 | 67 | 17 | 74 | HARDROCK | |||||||||||
750.45 | 750.45 | 149-900A-80R-2,28-31 | RUN CAB; REP P | 10 | 11 | 2 | 172 | 10 | 62 | 104 | 391 | 410 | 95 | 27 | 54 | HARDROCK | |||||||||||
750.45 | 750.45 | 149-900A-80R-2,28-31 | RUN CAD; REP A | 9.27 | 45.98 | 0.12 | 17.36 | 10.17 | 0.41 | 17.10 | 6.29 | 1.41 | 0.41 | 0.03 | HARDROCK-after XRF upgrade | ||||||||||||
750.60 | 750.60 | 149-900A-80R-2,43-46 | RUN CAJ; REP P | 11 | 13 | 5 | 188 | 11 | 45 | 33 | 239 | 460 | 115 | 22 | 71 | HARDROCK | |||||||||||
758.66 | 758.66 | 149-900A-81R-1,16-18 | RUN CAB; REP P | 11 | 22 | 15 | 213 | 7 | 39 | 5 | 200 | 393 | 220 | 31 | 43 | HARDROCK | |||||||||||
758.66 | 758.66 | 149-900A-81R-1,16-18 | RUN CAD; REP A | 2.83 | 53.48 | 1.11 | 14.45 | 8.91 | 0.16 | 11.07 | 7.03 | 3.65 | 0.28 | 0.02 | HARDROCK-after XRF upgrade | ||||||||||||
759.33 | 759.33 | 149-900A-81R-1,83-86 | RUN CAJ; REP P | 11 | 24 | 15 | 245 | 15 | 40 | 10 | 225 | 405 | 279 | 15 | 106 | HARDROCK | |||||||||||
760.66 | 760.66 | 149-900A-81R-2,74-77 | RUN CAJ; REP P | 11 | 15 | 9 | 191 | 8 | 59 | 58 | 162 | 428 | 271 | 7 | 96 | HARDROCK | |||||||||||
768.67 | 768.67 | 149-900A-82R-1,87-90 | RUN CAJ; REP P | 11 | 17 | 5 | 236 | 11 | 17 | 2 | 184 | 931 | 173 | 16 | 77 | HARDROCK | |||||||||||
770.43 | 770.43 | 149-900A-82R-2,128-132 | RUN CAC; REP P | 11 | 12 | 3 | 135 | 6 | 29 | 0 | 361 | 280 | 85 | 30 | 15 | HARDROCK | |||||||||||
770.43 | 770.43 | 149-900A-82R-2,128-132 | RUN CAF; REP A | 6.50 | 45.81 | 0.19 | 16.47 | 10.60 | 0.14 | 16.82 | 6.55 | 1.95 | 0.23 | HARDROCK-after XRF upgrade | |||||||||||||
771.06 | 771.06 | 149-900A-82R-3,52-55 | RUN CAJ; REP P | 11 | 18 | 3 | 339 | 11 | 17 | 0 | 218 | 397 | 122 | 35 | 56 | HARDROCK | |||||||||||
773.58 | 773.58 | 149-900A-82R-5,54-57 | RUN CAK; REP P | 11 | 24 | 4 | 437 | 19 | 17 | 5 | 192 | 433 | 176 | 20 | 168 | HARDROCK | |||||||||||
774.46 | 774.46 | 149-900A-83R-1,46-49 | RUN CAK; REP P | 11 | 12 | 4 | 116 | 9 | 32 | 18 | 210 | 774 | 166 | 8 | 49 | HARDROCK | |||||||||||
776.13 | 776.13 | 149-900A-83R-2,81-83 | RUN CAK; REP P | 11 | 17 | 4 | 247 | 8 | 21 | 0 | 176 | 563 | 131 | 15 | 54 | HARDROCK | |||||||||||
776.20 | 776.20 | 149-900A-83R-2,88-90 | RUN CAC; REP P | 12 | 17 | 2 | 248 | 8 | 23 | 0 | 245 | 309 | 92 | 16 | 100 | HARDROCK | |||||||||||
776.20 | 776.20 | 149-900A-83R-2,88-90 | RUN CAF; REP A | 3.22 | 47.28 | 0.15 | 20.88 | 7.21 | 0.11 | 9.37 | 10.98 | 1.61 | 0.56 | HARDROCK-after XRF upgrade | |||||||||||||
777.68 | 777.68 | 149-900A-84R-1,18-21 | RUN CAE; REP P | 11 | 17 | 2 | 306 | 9 | 35 | 5 | 230 | 531 | 147 | 40 | 43 | HARDROCK | |||||||||||
777.68 | 777.68 | 149-900A-84R-1,18-21 | RUN CAG; REP A | 4.95 | 48.14 | 0.23 | 20.35 | 8.38 | 0.13 | 10.74 | 9.23 | 2.07 | 0.74 | 0.01 | HARDROCK-after XRF upgrade | ||||||||||||
778.31 | 778.31 | 149-900A-84R-1,81-84 | RUN CAK; REP P | 11 | 14 | 2 | 281 | 10 | 33 | 11 | 194 | 297 | 92 | 17 | 34 | HARDROCK | |||||||||||
781.11 | 781.11 | 149-900A-84R-3,77-80 | RUN CAK; REP P | 10 | 15 | 3 | 290 | 13 | 24 | 23 | 170 | 177 | 97 | 26 | 27 | HARDROCK | |||||||||||
781.69 | 781.69 | 149-900A-84R-3,135-138 | RUN CAE; REP P | 10 | 16 | 2 | 302 | 11 | 13 | 2 | 196 | 192 | 64 | 19 | 68 | HARDROCK | |||||||||||
781.69 | 781.69 | 149-900A-84R-3,135-138 | RUN CAG; REP A | 3.33 | 50.31 | 0.17 | 22.52 | 5.95 | 0.08 | 8.41 | 10.18 | 1.83 | 0.78 | HARDROCK-after XRF upgrade | |||||||||||||
787.24 | 787.24 | 149-900A-85R-1,54-56 | RUN CAH; REP P | 10 | 15 | 6 | 167 | 5 | 33 | 2 | 261 | 1074 | 195 | 9 | 55 | HARDROCK | |||||||||||
787.24 | 787.24 | 149-900A-85R-1,54-56 | RUN CAI; REP A | 2.70 | 48.17 | 0.27 | 15.17 | 7.99 | 0.14 | 13.05 | 14.52 | 0.99 | 0.05 | HARDROCK-after XRF upgrade | |||||||||||||
789.64 | 789.64 | 149-900A-85R-3,50-54 | RUN CAH; REP P | 10 | 11 | 1 | 179 | 17 | 29 | 0 | 337 | 52 | 35 | 23 | 43 | HARDROCK | |||||||||||
789.64 | 789.64 | 149-900A-85R-3,50-54 | RUN CAI; REP A | 5.57 | 46.92 | 0.07 | 21.56 | 9.51 | 0.11 | 12.31 | 7.28 | 0.84 | 1.29 | HARDROCK-after XRF upgrade | |||||||||||||
792.53 | 792.53 | 149-900A-85R-5,76-79 | RUN CAH; REP P | 11 | 19 | 6 | 242 | 7 | 27 | 4 | 213 | 737 | 173 | 5 | 68 | HARDROCK | |||||||||||
792.53 | 792.53 | 149-900A-85R-5,76-79 | RUN CAI; REP A | 2.98 | 48.67 | 0.32 | 18.24 | 7.03 | 0.12 | 11.11 | 12.49 | 1.70 | 0.29 | HARDROCK-after XRF upgrade |